Product Description

PICC Mortar Concrete Chemical we have is a double-component mortar. This kind of chemical guarantees great abrasion resistance, high compression strength, low porosity, and outstanding bond with any surface such as PVC, steel, stone, concrete and so on. The key constituent of this type of chemical is ceramic ironite, which has excellent UV stability. Ideal for surface preparation, bonding for the old surface to new mortar, top seal, and primer coating, the PICC Mortar Concrete Chemical is absolutely safe for handing, non-toxic, long term adhesion, and applicable on both wet and dry surface.

Technical Specification

Property

Test Method/Standard

Result value

Primer

Viscosoity  of  bonding primer  kelox R101 :  Kelox  H404  (100:50by weight )

Brookfield viscosity standard

6510 cps

Pot life

 

70-90 minutes

PICC Mortar 

Density of Mortar 

 

2300 to 2370 kg/m3

Flow

IS 2250

25 to  30 %

Unconfined compressive strength

IS  456 & IS 6512

439-490 kg/cm3

Tensile  strength

IS 6512

30-37 kg/cm3

Abrasion  resistance (loss in weight per  unit area)

Method developed on basis of the abrasion measurement using dory abrasion IS 6512machine

0.40to 0.44gm/cm2

Static modulus  of elasticity

IS 456

2.4x105 to 3.2 x 105 kg/cm3

Flexural strength

IS 6512

45-50kg/cm3

Modulus of  rupture

IS 456

3x105 to 3.5 x 105 kg/cm3

Direct  bond strength (prism test) with primer at interface old concrete to fresh mortar

Technical Memorandum  CWPRS-February 2007

10-13 kg/cm3

Shear  strength (cone test ) with  primer at interface

ASTM C 882-99

50-55 kg/cm3

Direct bond strength  (prism  test ) with primer at interface dry bonding surface

Technical Memorandum  CWPRS-February 2007

15-17 kg/cm3

Direct bond strength with rock with primer at interface

Methodology developed at CWPRS

12-16 kg/cm3

Double shear strength

US  army corps  of  engineers

5-8 kg/cm3

Permeability  (K) with seal coat

IS 3085

<10 12 cm/sec

UV resistance

IS 101 Part 6 section 5)

168 hrs

Skin irritation

OECD 10993-11:  2006 (E)

Non-irritant

Toxicity test

ASTM C- 1202/AASHTO:T277

Avg .883  Coulombs

RCPT Test (Chloride ion penetration

IS 2584: 1963  Reffirmed 2006

10.3 kv

Break down voltage test

AAS Method

0.001%  by mass

Lead  content

On the lines of ASTM D543

After 24 hr decomposition discoloration  swelling  clouding tackiness rubberiness crazing bubbling solubility


DIMPLE CHEMICALS & SERVICES PRIVATE LIMITED

* Tips on getting accurate quotes. Please include product name, order quantity, usage, special requests if any in your inquiry.



Back to top
DIMPLE CHEMICALS & SERVICES PVT. LTD. All Rights Reserved.(Terms of Use)
Developed and Managed by Infocom Network Ltd.